Ador TK 85
Package á 25 g
High gold-containing casting alloy
Aufgrund der aktuellen Rohstoffpreisentwicklung werden alle Legierungen vorerst auf Tagespreisbasis veröffentlicht. Die Preise werden jeden Morgen um 11 Uhr aktualisiert.
133,19 € excl. VAT
Description
>>> GebrAnw-Dental-Base-Alloy-TK-85.pdf <<<
| Type: | High gold-containing dental casting alloy on the gold basis, type 4 (extra hard)
acc. DIN EN ISO 22674 |
| Colour: | yellow |
| Applicable scope: | Inlays, Onlays | ● |
| Crowns | ● | |
| Small bridges | ● | |
| Bridges of any physiological span | ● | |
| Milling, cone and attachment works | ● | |
| Modeling casting |
| Composition: | Au | 85,30 |
| (mass fraction in %) | Pt | 9,90 |
| Ir | 0,10 | |
| Rh | 0,70 | |
| Zn | 3,00 | |
| In | 1,00 |
| Technical specifications: | Density in g/cm³ | 18,2 |
| Vickers hardness HV 5/30 | (s) 180 (a-s) 200 | |
| Yield strength Rp0,2 in MPa | (s) 410 (a-s) 500 | |
| Elongation at break in % | (s) 4 (a-s) 4 | |
| Elastic modulus in GPa | 100 | |
| Melting interval in °C | 950 – 1070 |
| Processing: | Preheating temp. of the casting moulds in °C | 800 |
| Casting temperature in °C | 1220 | |
| Crucibles | Graphite/ceramic | |
| Curing | 450°C/15min |
| Suitable solders: | Joints as modeling alloy | AL 800 Lot |
| Joints as modeling alloy | AL 750 Lot |
1) Brief description:
s – self-curing, n – after ceramic firing, a-s – curing from s condition
a-n – curing from n condition
2) All information about cured condition is given according to the alloy:
– Oxide firing 10min/ 960°C + 4x4min/ 960°C for yellow conventional bonding alloys
– Oxide firing 10min/ 980°C + 4x4min/ 980°C for white conventional bonding alloys
– Oxide firing 10min/ 800°C + 4x4min/ 800°C for LFC-systems
Corresponding data are true under these conditions only.
3) The ceramic firing should be carried out according to the manufacturer's instructions.
Additional information
| Weight | 33 g |
|---|