Type: Gold-reduced metal-ceramic alloy on the gold basis, type 4 (extra hard)

acc. DIN EN ISO 22674

Colour: white

 

Applicable scope: Inlays, Onlays
Crowns
Small bridges
Large-span bridges
Milling, cone and attachment works
Modeling casting

 

Composition: Au 51,60
(mass fraction in %) Pd 38,40
Ir 0,05
Ru 0,05
In 8,40
Ga 1,50

 

Technical specifications: Density in g/cm³ 13,8
Vickers hardness HV 5/30 (s)220 (n)220 (a-n)230
Yield strength Rp0,2 in MPa (s)470 (n)530 (a-n)560
Elongation at break in % (s)31 (n)30 (a-n)29
Average linear CTE 25 – 500 °C in 10-6 K-1 13,5
Average linear CTE 25 – 600 °C in 10-6 K-1 13,8
Elastic modulus in GPa 110
Melting interval in °C 1200 - 1310

 

Processing: Preheating temp. of the casting moulds in °C 900
Casting temperature in °C 1460
Crucibles Ceramic
Curing 500°C/15min

 

Suitable solders: Joints before ceramic firing AL 1060 W
Joints after ceramic firing AL 750

 

1) Brief description:

s – self-curing, n – after ceramic firing, a-s – curing from s condition

a-n – curing from n condition

 

2) All information about cured condition is given according to the alloy:

– Oxide firing 10min/ 960°C + 4x4min/ 960°C for yellow conventional bonding alloys

– Oxide firing 10min/ 980°C + 4x4min/ 980°C for white conventional bonding alloys

– Oxide firing 10min/ 800°C + 4x4min/ 800°C for LFC-systems

Corresponding data are true under these conditions only.

 

3) The ceramic firing should be carried out according to the manufacturer's instructions.