ADORNOVA PdF
Package á 25 g
High gold-containing multi-purpose alloy
Aufgrund der aktuellen Rohstoffpreisentwicklung werden alle Legierungen vorerst auf Tagespreisbasis veröffentlicht. Die Preise werden jeden Morgen um 11 Uhr aktualisiert.
120,93 € excl. VAT
Description
>>> GebrAnw-Dental-Base-Alloy-Adornova-Pdf.pdf <<<
| Type: | High gold-containing precious alloy on the gold basis intended for metal-ceramic dentures or for dental casting alloy, type 3 (hard), type 4 (extra hard) for n/a-n
acc. DIN EN ISO 22674 |
| Colour: | yellow |
| Applicable scope: | Inlays, Onlays | ● |
| Crowns | ● | |
| Small bridges | ● | |
| Medium-sized bridges | ● | |
| Milling, cone and attachment works | ● | |
| Modeling casting | ● | |
| Applicable for LCF (Carrara-Type) | ● |
| Composition: | Au | 75,00 |
| (mass fraction in %) | Pt | 9,10 |
| Rh | 0,60 | |
| Ir | 0,10 | |
| Ag | 13,10 | |
| Zn | 2,00 | |
| Ta | 0,10 |
| Technical specifications: | Density in g/cm³ | 16,7 | |||
| Vickers hardness HV 5/30 | as modeling alloy | (s) 140 | (a-s) 150 | ||
| as bonding alloy | (s) 140 | (n) 190 | (a-n) 200 | ||
| Yield strength Rp0,2 in MPa | as modeling alloy | (s) 320 | (a-s) 330 | ||
| as bonding alloy | (s) 320 | (n) 420 | (a-n) 450 | ||
| Elongation at break in % | as modeling alloy | (s) 15 | (a-s) 15 | ||
| as bonding alloy | (s) 15 | (n) 5 | (a-n) 5 | ||
| Average linear CTE 25 – 500 °C in 10-6 K-1 | 15,8 | ||||
| Average linear CTE 25 – 600 °C in 10-6 K-1 | 16,2 | ||||
| Elastic modulus in GPa | 100 | ||||
| Melting interval in °C | 1020 – 1090 |
| Processing: | Preheating temp. of the casting moulds in °C | 750 | |
| Casting temperature in °C | 1240 | ||
| Crucibles | Graphite/ceramic | ||
| Oxide firing | 800°C | ||
| Curing | (a-s) | 450°C/15min. | |
| (a-n) | 550°C/15min. |
| Suitable solders: | Joints before ceramic firing | AL 920 |
| Joints after ceramic firing | AL 700 PF | |
| Joints as modeling alloy | AL 750 |
1) Brief description:
s – self-curing, n – after ceramic firing, a-s – curing from s condition
a-n – curing from n condition
2) All information about cured condition is given according to the alloy:
– Oxide firing 10min/ 960°C + 4x4min/ 960°C for yellow conventional bonding alloys
– Oxide firing 10min/ 980°C + 4x4min/ 980°C for white conventional bonding alloys
– Oxide firing 10min/ 800°C + 4x4min/ 800°C for LFC-systems
Corresponding data are true under these conditions only.
3) The ceramic firing should be carried out according to the manufacturer's instructions.
Additional information
| Weight | 33 g |
|---|
Only logged in customers who have purchased this product may leave a review.